Internal structure change of carbon tool steel after heat treatment / Chew, Chun Chi

By:

Chew, Chun Chi

Material type: Text

TextPublication details: Kuantan, Pahang : UMP, 2008Description: 55 p. : ill. (some col.) ; 30 cm. + 1 computer discISBN:

THE0007407(Local)

Other title:

Internal structure change of carbon tool steel after heat treatment [electronic resource]

Subject(s):

Dissertation note: Project paper (Bachelor of Mechanical Engineering with Manufacturing) -- Universiti Malaysia Pahang - 2008 Abstract: Carbon steel is normally used in the manufacture of chisels, tools parts where high hardness is required to maintain a sharp cutting edge. But, the most common problems we encountered are the short life of the tool. Hence, it is important to use a suitable medium for quenching process to extend the tool life. The main objective of this project is to analyze the internal structure of carbon steel after quenching process. Eventually, the most suitable medium for quenching carbon steel AISI 1045 will be recommended. A carbon steel rod with a diameter of 1.6cm was cut into the size of 2cm in length. Six specimens in the same dimensions were prepared. Each specimen’s surface was ground by using different grade of abrasive paper. After the grinding process, three out of six specimens were undergoing quenching process for one day in three different types of medium; which is oil, water and coolant. However, another three specimens were quenched for one day. After quenching process, all specimens were grinding again to retain shining surface. Diamond liquid was used to polish the surface and then the surface was etched by 2% nital. The internal structure of water and coolant quenching formed finer pearlite while oil quenching formed coarser pearlite. The structures formed have high hardness value ranged from 20.3 HRC to 47.5 HRC. The results were analyzed by using Rockwell hardness tester. The internal structure of specimen was analysed using microscope image analyser equipment and the results were displayed onto computer screen.-Author-

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings ( 2 )
Title notes ( 2 )

Holdings
Item type	Current library	Call number	Copy number	Status	Date due	Barcode
Final Year Report	UMPLIB PEKAN	TN672 .C44 2008 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000038202
Final Year Report	UMPLIB PEKAN	CD 3454 \| TN672 .C44 2008 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000038203

Project paper (Bachelor of Mechanical Engineering with Manufacturing) -- Universiti Malaysia Pahang - 2008

Carbon steel is normally used in the manufacture of chisels, tools parts where high hardness is required to maintain a sharp cutting edge. But, the most common problems we encountered are the short life of the tool. Hence, it is important to use a suitable medium for quenching process to extend the tool life. The main objective of this project is to analyze the internal structure of carbon steel after quenching process. Eventually, the most suitable medium for quenching carbon steel AISI 1045 will be recommended. A carbon steel rod with a diameter of 1.6cm was cut into the size of 2cm in length. Six specimens in the same dimensions were prepared. Each specimen’s surface was ground by using different grade of abrasive paper. After the grinding process, three out of six specimens were undergoing quenching process for one day in three different types of medium; which is oil, water and coolant. However, another three specimens were quenched for one day. After quenching process, all specimens were grinding again to retain shining surface. Diamond liquid was used to polish the surface and then the surface was etched by 2% nital. The internal structure of water and coolant quenching formed finer pearlite while oil quenching formed coarser pearlite. The structures formed have high hardness value ranged from 20.3 HRC to 47.5 HRC. The results were analyzed by using Rockwell hardness tester. The internal structure of specimen was analysed using microscope image analyser equipment and the results were displayed onto computer screen.-Author-