Investigation of mig welding on dissimilar thickness of metal sheets (steel and stainless steel) / Mohd Iqbal Abd Razak

By:

Mohd Iqbal Abd Razak

Material type: Text

TextPublication details: Kuantan, Pahang : UMP, 2012Description: xii, 66 p. : ill. (some col.) ; 30 cm. + 1 CD-ROMISBN:

THE0005726(Local)

Subject(s):

Dissertation note: Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2012 Abstract: Based on different welding parameters, a welding process between mild steel and stainless steel were performed in this experiment using metal inert gas (MIG) machine. The objective of this experiment was to investigate the effect of welding voltages (15V, 20V and 25V) wire feed rates (80 ipm and 100ipm) and filler metals (ER70S-6 and ER308L) to the microstructure and mechanical properties of the welded mild steel to stainless steel specimens. The microstructure changes and the mechanical properties result from tensile and hardness test were analyzed and compared between the welded zones, heat affected zone (HAZ) and base metal. From the results obtained the grain size of weld zone and HAZ increases when the welding voltage and wire feed rate increases. The strength of the welded joint was directly proportional to the increasing in voltage and wire feed rate but their hardness value was irreversibly proportional towards the increasing parameter value. Filler metal of ER70S-6 shows better result in hardness test while filler metal of ER308L shows better strength in the joint. In conclusion, increasing voltage and wire feed rate will increases the strength but lowered the hardness of the joint. Filler ER308L was suitable to be used to increase strength of the joint while filler ER70S-6 was more suitable in increasing the hardness of the joint.

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings ( 2 )
Title notes ( 3 )

Holdings
Item type	Current library	Call number	Copy number	Status	Date due	Barcode
Final Year Report	UMPLIB PEKAN	CD 6635 \| TA417.7.T4 I63 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000069769
Final Year Report	UMPLIB PEKAN	TA417.7.T4 I63 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000069768

Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2012

Bibliography: p. 55-56

Based on different welding parameters, a welding process between mild steel and stainless steel were performed in this experiment using metal inert gas (MIG) machine. The objective of this experiment was to investigate the effect of welding voltages (15V, 20V and 25V) wire feed rates (80 ipm and 100ipm) and filler metals (ER70S-6 and ER308L) to the microstructure and mechanical properties of the welded mild steel to stainless steel specimens. The microstructure changes and the mechanical properties result from tensile and hardness test were analyzed and compared between the welded zones, heat affected zone (HAZ) and base metal. From the results obtained the grain size of weld zone and HAZ increases when the welding voltage and wire feed rate increases. The strength of the welded joint was directly proportional to the increasing in voltage and wire feed rate but their hardness value was irreversibly proportional towards the increasing parameter value. Filler metal of ER70S-6 shows better result in hardness test while filler metal of ER308L shows better strength in the joint. In conclusion, increasing voltage and wire feed rate will increases the strength but lowered the hardness of the joint. Filler ER308L was suitable to be used to increase strength of the joint while filler ER70S-6 was more suitable in increasing the hardness of the joint.