Comparison of erosion corrosion of titanium and stainless steel in seawater / Mohamad Izwan Abdul Ghani

By:

Mohamad Izwan Abdul Ghani

Material type: Text

TextPublication details: Kuantan, Pahang : UMP, 2012Description: xviii, 71 p. : ill. (some col.) ; 30 cm. + 1 CD-ROMISBN:

THE0005879(Local)

Subject(s):

Dissertation note: Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2012 Abstract: The application of Stainless steel and Titanium alloy had been rising in marine application that promoted this study to investigate erosion corrosion behaviour for Stainless steel grade 301 and Titanium. Erosion corrosion test were conducted for both material at constant rate velocity, 900 rpm and at ambient temperature in the range 27oC-30oC. The erosion corrosion were carried out by immersing specimens in an aqueous 3.5%NaCl and presence of 10 wt % sand particles. The erosion corrosion tests were done by using electrochemical test which involve oxidation and reduction process. Graphite is use as counter electrode while specimens as working electrode and saturated calomel electrode (SCE) as reference electrode. Potentiodynamic polarization has been carried out by using potentiostat model WPG100i with potential scan rate use is 20 and potential range of -0.8V until 0.2V. Analysis of image and surface roughness, were taken before and after erosion corrosion test. Titanium alloy show small pitting form and low value of surface roughness compare to Stainless steel. The full observation on the result from the test shows that corrosion rate of Stainless steel is higher than the corrosion rate for Titanium alloy.

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings ( 2 )
Title notes ( 3 )

Holdings
Item type	Current library	Call number	Copy number	Status	Date due	Barcode
Final Year Report	UMPLIB PEKAN	TA462 .I99 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000069778
Final Year Report	UMPLIB PEKAN	CD 6640 \| TA462 .I99 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000069779

Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2012

Bibliography : p. 66-67

The application of Stainless steel and Titanium alloy had been rising in marine application that promoted this study to investigate erosion corrosion behaviour for Stainless steel grade 301 and Titanium. Erosion corrosion test were conducted for both material at constant rate velocity, 900 rpm and at ambient temperature in the range 27oC-30oC. The erosion corrosion were carried out by immersing specimens in an aqueous 3.5%NaCl and presence of 10 wt % sand particles. The erosion corrosion tests were done by using electrochemical test which involve oxidation and reduction process. Graphite is use as counter electrode while specimens as working electrode and saturated calomel electrode (SCE) as reference electrode. Potentiodynamic polarization has been carried out by using potentiostat model WPG100i with potential scan rate use is 20 and potential range of -0.8V until 0.2V. Analysis of image and surface roughness, were taken before and after erosion corrosion test. Titanium alloy show small pitting form and low value of surface roughness compare to Stainless steel. The full observation on the result from the test shows that corrosion rate of Stainless steel is higher than the corrosion rate for Titanium alloy.