Normal view MARC view ISBD view

Parametric study on fatique failure using crack initiation method/ Mohd Fadzrul Hisyam Badarudin

By:

Mohd Fadzrul Hisyam Badarudin

Material type: Text

TextPublication details: Kuantan, Pahang : UMP, 2012Description: xviii, 79 p. : ill. (some col.) ; 30 cm.+ 1 CD-ROMISBN:

THE0005747(Local)

Subject(s):

Dissertation note: Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2012 Abstract: This thesis presents the parametric study on fatigue failure using crack initiation method analysis. In order to investigate the fatigue failure of AISI/SAE 1045 steel by varying the microstrain parameters under different loading cases and predict the crack initiation life, compact tension specimen model is used for this project. The finite element linear static analysis is done by using MSC Patran 2010 and MSC Nastran 2007 to determine the result of the stress distribution on the model. The fatigue analysis is conducted by using ANSYS 13.0 nCode Design Life to determine the microstrain value that initiates the dynamic and static failure under three loading cases; compression-compression, compression-tension and tension-tension. The obtained microstrain values are then used to obtain the fatigue damage, D which is then used to predict the crack initiation life of the material. Using Palmgren-Milner rule, the value of D will obtain the crack initiation life cycle of the material, Nf. Based on the result, it has found that the most critical loading case for the fatigue and static failure are the tension-tension. The crack initiation life of the material is at high cycle fatigue, and able to stand about 5 × 106 cycles without failure for every loading case. Meanwhile the static failure analysis has found that there is no crack initiation life, as it has failed at very low cycle in every loading case.

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings ( 2 )
Title notes ( 3 )

Holdings
Item type	Current library	Call number	Copy number	Status	Date due	Barcode
Final Year Report	UMPLIB PEKAN	TA418.38 .F33 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000069749
Final Year Report	UMPLIB PEKAN	CD6627 \| TA418.38 .F33 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000069750

Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2012

Bibliography: p.78-79

This thesis presents the parametric study on fatigue failure using crack initiation method analysis. In order to investigate the fatigue failure of AISI/SAE 1045 steel by varying the microstrain parameters under different loading cases and predict the crack initiation life, compact tension specimen model is used for this project. The finite element linear static analysis is done by using MSC Patran 2010 and MSC Nastran 2007 to determine the result of the stress distribution on the model. The fatigue analysis is conducted by using ANSYS 13.0 nCode Design Life to determine the microstrain value that initiates the dynamic and static failure under three loading cases; compression-compression, compression-tension and tension-tension. The obtained microstrain values are then used to obtain the fatigue damage, D which is then used to predict the crack initiation life of the material. Using Palmgren-Milner rule, the value of D will obtain the crack initiation life cycle of the material, Nf. Based on the result, it has found that the most critical loading case for the fatigue and static failure are the tension-tension. The crack initiation life of the material is at high cycle fatigue, and able to stand about 5 × 106 cycles without failure for every loading case. Meanwhile the static failure analysis has found that there is no crack initiation life, as it has failed at very low cycle in every loading case.