Effect of specimen size on fracture toughness of mild steel / Mohd Syafiq Mohd Saufi

By:

Mohd Syafiq Mohd Saufi

Material type: Text

TextPublication details: Kuantan, Pahang : UMP, 2012Description: xiv, 72 p. : ill. ; 30 cm. + 1 CD-ROMISBN:

THE0005870(Local)

Subject(s):

Dissertation note: Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang – 2012 Abstract: This project was conducted to investigate the effect of specimen size on fracture toughness of mild steel. Fracture toughness is an indication of the amount of stress required to propagate a pre-existing flaw. It is a very important material property since the occurrence of flaws is not completely avoidable in the processing, fabrication, service of a material or component. In this experiment, the specimen size was chosen as a main parameter to analyse the fracture toughness of mild steel. The specimen size was divided into two parameter to be investigated, there is thickness and notch depth of the specimen. The specimen geometry was referred to the ASTM E399-74 standard and the test applied for the fracture toughness is single edge notch bending. From the test results, when the thickness of the specimen increase the fracture decreases until the thickness reach the critical dimension and the fracture was become constant. For the notch depth, when the notch depth decreases the fracture of the specimen also decreases until the notch depth reach the critical dimension and the fracture toughness was become constant. The thickness and notch depth of the specimen is main parameter to analyze the fracture toughness of the material or specimen because each of the specimens will reach the critical dimension and constant the fracture toughness value.

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings ( 2 )
Title notes ( 3 )

Holdings
Item type	Current library	Call number	Copy number	Status	Date due	Barcode
Final Year Report	UMPLIB PEKAN	TA460 .S93 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000076075
Final Year Report	UMPLIB PEKAN	CD 7299 \| TA460 .S93 2012 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000076076

Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang – 2012

Bibliography : p. 70-72

This project was conducted to investigate the effect of specimen size on fracture toughness of mild steel. Fracture toughness is an indication of the amount of stress required to propagate a pre-existing flaw. It is a very important material property since the occurrence of flaws is not completely avoidable in the processing, fabrication, service of a material or component. In this experiment, the specimen size was chosen as a main parameter to analyse the fracture toughness of mild steel. The specimen size was divided into two parameter to be investigated, there is thickness and notch depth of the specimen. The specimen geometry was referred to the ASTM E399-74 standard and the test applied for the fracture toughness is single edge notch bending. From the test results, when the thickness of the specimen increase the fracture decreases until the thickness reach the critical dimension and the fracture was become constant. For the notch depth, when the notch depth decreases the fracture of the specimen also decreases until the notch depth reach the critical dimension and the fracture toughness was become constant. The thickness and notch depth of the specimen is main parameter to analyze the fracture toughness of the material or specimen because each of the specimens will reach the critical dimension and constant the fracture toughness value.