03352ntm a2200337 i 4500 0 0 lcc 0 1 20000 20000 2025-05-15 0 FTKPM .M87 2025 r Thesis T000003569 2025-05-15 00:00:00 2025-05-15 THESIS 0 0 lcc 0 -2 20000 20000 2025-05-15 0 CD13763 T000003570 2025-05-15 00:00:00 2025-05-15 THESIS 102539 102545 MY-KuUP 20251125111041.0 t||||fr|||| 000 0 ta 250515t20252025my a|||fr|||| 000 0 eng d THE0010073 (Local) Hardback UMPSA eng UMPSA rda FTKPM .M87 2025 r Thesis Raja Murfiqah Raja Mohamad Fouzy, author. Investigation of microlens array (MLA) replicated on polymer and glass substrates using partial filling hot embossing assisted with CO2 laser irradiation / Raja Murfiqah Binti Raja Mohamad Fouzy Kuantan, Pahang : UMPSA , 2025 © 2025 xvii, 142 pages : illustrations ; 30 cm. + 1 CD-ROM rdacontent text rdamedia unmediated rdacarrier volume rda text file PDF Faculty of Manufacturing & Mechatronics Engineering Technology Thesis (Doctor of Philosophy) -- Universiti Malaysia Pahang – 2025 Includes bibliographical references Micro/nanostructures are essential in advanced technologies across industries such as biomedical, electronics, imaging, and optics. This study explores the integration of partial filling hot embossing (PFHE) with CO₂ laser irradiation for fabricating microlens arrays (MLAs) on polymer and glass substrates. The CO₂ laser eliminates the need for preheating, soaking, holding, and cooling steps, reducing thermal cycle time from 15 minutes to under 10 seconds. This approach enhances efficiency and reduces costs compared to conventional hot embossing. Conventional hot embossing experiments demonstrated that temperature, pressing load, and holding time significantly influence replication quality. Elevated temperatures soften thermoplastic materials like PMMA, improving mold filling through reduced viscosity. An optimal pressing load (1 MPa) ensures complete mold cavity filling, while insufficient load leads to incomplete formation. Similarly, holding time of 6 minutes produces precise MLA features by allowing thorough material flow, compared to inadequate results at shorter durations. The PFHE method with CO₂ laser irradiation leverages silicon molds' high transmittance and PMMA's strong optical absorption at a 10.6 μm wavelength. Optimized parameters— laser power (30 W), scanning speed (100 mm/s), and irradiation time (9 s)—achieve MLAs with lens diameters of 100 μm, 300 μm, and 500 μm, alongside a smooth surface finish (roughness of 0.032 μm). Lower power levels, insufficient irradiation times, or high scanning speeds result in incomplete patterns, while prolonged heating at slower scanning speeds (50 mm/s) causes deformation. This approach not only addresses challenges of conventional hot embossing but also enhances mold durability and process efficiency. The PFHE with CO₂ laser irradiation offers a fast, low-cost, and highthroughput solution for MLA fabrication, demonstrating strong potential for industrial applications and significant cost savings. Faculty of Manufacturing & Mechatronics Engineering Technology Dissertations Universities and colleges Dissertations Theses Dissertations lcc THESIS