02703nam a2200265 a 4500 vtls000058167 KUKTEM 20251114204509.0 120109t2010 my a f m 000 0 eng d THE0004852(Local) 201905161134 smfh 201201091328 ida UMP TP757 .D59 2010 rs Bc. Diyana Ghazali A study of corrosion to the carbon steel in the present of carbon dioxide / Diyana Ghazali Kuantan, Pahang : UMP, 2010 xiii, 39 p. : ill. ; 30 cm. + 1 CD-ROM Project paper (Bachelor of Chemical Engineering (Gas Technology)) -- Universiti Malaysia Pahang - 2010 Bibliography : p. 29-31 The study describes on effect of several environmental factors of the corrosion rate in the pipeline. Transmission gas pipeline is an important part of oil and gas industries and the carbon steel is a primary material for construction the pipeline due to its low cost and availability, but it is very susceptible to corrosion in CO2 environments. Carbon dioxide (CO2) corrosion is the major problem in oil and gas industries that causes the pipeline failures. Aqueous carbon dioxide (carbonic acid) is corrosive and corrodes the carbon steel pipelines and it is influenced by several environmental factors such as pH, temperature, partial pressure of CO2, hydrodynamics, etc. Actually there are many types of corrosion which occur in pipeline but in this study only focused on CO2 corrosion and only two environmental factors which is pH and temperature were investigated. In this study, SOLTEQ Corrosion Study Kits, Model BP01 is used as an apparatus to examine the corrosion rate of metal. Based on the result from the experiment, it was stated that acidic condition recorded the corrosion rate of weight loss was very high. In the temperature test with 3.5% NaCl solution, corrosion rate was high at temperature 1200C. From the research, the corrosion occured in high temperature condition and at low pH environment. As the temperature increase, the corrosion rate also increases due to the dissolution of iron ion and formation of weak carbonic acid. The weak carbonic acid dissociates into carbonate and hydrogen ion, which increase the cathodic reaction on the metal surface. In acidic condition, the available H+ ions makes H+ reduction the dominating cathodic reaction and corrosion rate is found to be sensitive at this low pH. Gas pipelines Corrosion Carbon steel Corrosion Carbon dioxide 0 0 0 1 10000 10000 2019-09-04 0 TP757 .D59 2010 rs Bc. 0000060869 2019-09-04 00:00:00 1 2019-09-04 PSM 0 0 0 1 10000 10000 2019-09-04 0 CD 5600 | TP757 .D59 2010 rs Bc. 0000060870 2019-09-04 00:00:00 1 2019-09-04 PSM VIRTUA40 3042 3048 VTLSSORT0080*0200*0400*0900*1000*2450*2600*3000*5020*5040*5200*6500*6501*6502*9992