Mohd Faisal Ahmad Shafawi creator text theses my Kuantan, Pahang UMP 2010 monographic eng

print

xiv, 36 p. : ill. (some col.) ; 30 cm. + 1 CD-ROM The effects of filler loading on the tensile and elongation at break of SMR 10 using a sulphur vulcanization system was studied. Carbon black (N220) was used as the fillers and the loading range was from 10 to 40 phr. Two Roll Mill (Model LS-22005) and 25 Ton Hot Cold Molding Press (Model LS22025) used for mixing and molding press. Both equipments were supplied by Lotus Scientific. Tensile and elongation at break were determined using a Universal Testing Machine (Model 133004600771) operating at 20 mm/min. Results show that, elongation at break decreases, but tensile strength, increase with filler loading. This observation is attributed to the rubber–filler interphaseinteraction of carbon black and rubber. specialized Mohd Faisal Ahmad Shafawi Project paper (Bachelor of Chemical Engineering) -- Universiti Malaysia Pahang - 2010 Includes bibliographical references Carbon-black Rubber Mechanical properties Rubber Additives THE0004881(Local) UMP 120313 20251114204513.0 vtls000058654