AU  - Mohd Faisal Ahmad Shafawi
TI  - Effect of carbon black loading on the mechanical properties of rubber vulcanizates
SN  - THE0004881(Local)
PY  - 2010///
CY  - Kuantan, Pahang
PB  - UMP
KW  - Carbon-black
KW  - Rubber
KW  - Mechanical properties
KW  - Additives
N1  - Project paper (Bachelor of Chemical Engineering) -- Universiti Malaysia Pahang - 2010; Includes bibliographical references
N2  - The effects of filler loading on the tensile and elongation at break of SMR 10 using a sulphur vulcanization system was studied. Carbon black (N220) was used as the fillers and the loading range was from 10 to 40 phr. Two Roll Mill (Model LS-22005) and 25 Ton Hot Cold Molding Press (Model LS22025) used for mixing and molding press. Both equipments were supplied by Lotus Scientific. Tensile and elongation at break were determined using a Universal Testing Machine (Model 133004600771) operating at 20 mm/min. Results show that, elongation at break decreases, but tensile strength, increase with filler loading. This observation is attributed to the rubber–filler interphaseinteraction of carbon black and rubber
ER  -