01835nam a2200265 a 4500 vtls000058678 KUKTEM 20251114204516.0 120315t2010 my a f m 001 0 eng d THE0004884(Local) 201905131230 SHAHRILJ 201203151629 Fida UMP TP951 .W37 2010 rs Bc. Mohd Waqiyuddin Mohd Salleh The effect of carbon black loadings on tensile strength of rubber vulcanizates / Mohd Waqiyuddin Mohd Salleh Kuantan, Pahang : UMP, 2010 xiii, 55 p. : ill. (some col.) ; 30 cm. + 1 CD-ROM Project paper (Bachelor of Chemical Engineering) -- Universiti Malaysia Pahang - 2010 Includes bibliographical references In this study, the effect of filler loadings (carbon black) on the tensile strength of SMR 10 was investigated. The carbon black grade was chosen N220 and the loading ranges were set 20, 40, 50, and 60 parts per hundred rubbers (phr). For the mixing and moulding process, the Two Roll Mill (Model LS-22005) and 25 Ton Hot Cold Molding Press (Model LS22025) was used which is supplied by Lotus Scientific. In order to determine the tensile strength values, a Universal Testing Machine (Model 133004600771) operating at 20 mm/min was used. It was found that the tensile strength increase with the increasing of carbon black loading until it reaches at the maximum interphase interaction between the polymer chains and filler. This observation is attributed to the rubber–filler interphase interaction of carbon black and rubber. Carbon-black Rubber Mechanical properties Rubber Additives 0 0 0 1 10000 10000 2019-09-04 0 TP951 .W37 2010 rs Bc. 0000063304 2019-09-04 00:00:00 1 2019-09-04 PSM 0 0 0 1 10000 10000 2019-09-04 0 CD 5890 | TP951 .W37 2010 rs Bc. 0000063305 2019-09-04 00:00:00 1 2019-09-04 PSM VIRTUA40 3248 3254 VTLSSORT0080*0200*0400*0900*1000*2450*2600*3000*5020*5040*5200*6500*6501*6502*9992