02064nam a2200241 a 4500 vtls000075776 KUKTEM 20251114204544.0 131029t2012 my da f abm 000 0 eng d THE0005902(Local) 201905141212 aida 201310291204 nabilah UMP TA467 .M66 2012 rs Bc. Mong, Bee Tong Outdoor-indoor corrosion of AISI 1010 steel in UMP Pekan / Mong Bee Tong Kuantan, Pahang : UMP, 2012 xiv, 71 p. : ill. ; 30 cm. + 1 CD-ROM Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang – 2012 Bibliography : p. 58-60 This project intends to study the outdoor and indoor atmospheric corrosion behavior of AISI 1010 steel over time of exposure in University Malaysia Pahang, Pekan. The project is an experimental analysis in which exposure tests were carried out in accordance to ASTM G1 and ASTM G50. The AISI 1010 steel were exposed for a total of 6 weeks from 1st March 2012 to 12th April 2012. In order to determine and evaluate the atmosphere characteristics, the atmospheric temperature, dew point temperature and relative humidity were monitored. The corrosion products were observed by visually and SEM analysis. It is found that the lepidocrocite and geothite are the major constituents of the corrosion product. Furthermore, the corrosion rate was obtained from the mass loss by applying the equation accordance to ASTM G50. It is noted that the mass loss of both indoor and outdoor atmosphere is increased but tended to stabilize over exposure time. However, the corrosion rate of the outdoor atmosphere is found higher compared to indoor exposure. As a result, the corrosion rate of AISI 1010 steel which exposed at University Malaysia Pahang, Pekan depends mainly on the type of atmospheres rather than time of exposure. Steel Corrosion 0 0 0 1 20000 20000 2019-09-04 0 TA467 .M66 2012 rs Bc. 0000076105 2019-09-04 00:00:00 1 2019-09-04 PSM 0 0 0 1 20000 20000 2019-09-04 0 CD 7314 | TA467 .M66 2012 rs Bc. 0000076106 2019-09-04 00:00:00 1 2019-09-04 PSM VIRTUA40 4041 4047 VTLSSORT0080*0200*0400*0900*1000*2450*2600*3000*5020*5040*5200*6500*9992