01958nam a2200253 a 4500 vtls000075777 KUKTEM 20251114204544.0 131029t2012 my da f abm 000 0 eng d THE0005904(Local) 201905141216 aida 201310291236 nabilah UMP TA467 .N35 2012 rs Bc. Mohd Khairul Na'im Mohd Ariffin Effect of velocity in erosion corrosion / Mohd Khairul Na'im Mohd Ariffin Kuantan, Pahang : UMP, 2012 xiv, 60 p. : ill. ; 30 cm. + 1 CD-ROM Project paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang – 2012 Bibliography : p. [55]-56 The present study has been conducted to investigate the interaction effect of velocity on erosion corrosion of material in aqueous slurries. Tests were performed on stainless steel samples of grade 301. Pure erosion and pure corrosion as well as erosion corrosion impingement tests were carried out at two different impact velocities 500 rpm, 1000 rpm and also without any velocity. The erosion corrosion test was carried out by immersing the specimen in an aqueous 3.5% NaCl solution and presence of sand particles. Electrochemical Erosion Corrosion Test have been conducted and reported in this thesis. The data then analyze using Ivman software to determine the value of corrosion rate. The surface image and surface roughness value was taken before and after the Electrochemical Erosion-Corrosion test. From observation of the result, when the value of velocity increases the corrosion rate also increases. Besides that, the value of surface roughness also increase when the corrosion rate increase due to present of pitting corrosion. Steel Erosion Corrosion and anti-corrosives 0 0 0 1 20000 20000 2019-09-04 0 TA467 .N35 2012 rs Bc. 0000076107 2019-09-04 00:00:00 1 2019-09-04 PSM 0 0 0 1 20000 20000 2019-09-04 0 CD 7315 | TA467 .N35 2012 rs Bc. 0000076108 2019-09-04 00:00:00 1 2019-09-04 PSM VIRTUA40 4049 4055 VTLSSORT0080*0200*0400*0900*1000*2450*2600*3000*5020*5040*5200*6500*6501*9992