02462ntm a2200289 a 4500 vtls000102314 KUKTEM 20251117113349.0 171031t2017 my a f a m 000 0 eng d THE0000137(Local) 201905131247 nazirah 201712061239 huda 201711011625 fateeha 201710311129 fateeha UMP FIST .F37 2017 r Bc. Nurul Farhana Ahmad Fabrication and characterization of PVA/starch fibre using electrospinning technique / Nurul Farhana Ahmad Kuantan, Pahang : UMP, 2017 24 p. : ill. ; 30 cm. + 1 CD-ROM Faculty of Industrial Sciences and Technology Project Paper (Bachelor of Applied Science (Hons.) Material Technology) -- Universiti Malaysia Pahang – 2017 Bibliography : p. 23-24 In this research the polyvinyl alcohol (PVA) and starch are synthesized for the fabrication of fibre using electrospinning method. The fabrication of fibre for this research were prepared using four different ratio which were 100:0, 80:20, 60:40 and 50:50 of PVA/starch. The weight percent for the PVA and starch were 15wt% respectively. The obtained fibre were observed under the Scanning Electron Microscope (SEM) for the determination of the average diameter. The average diameter obtained for the four samples are 290.18 ± 26.24, 202.19 ± 37.75, 142.43 ± 25.96, 64.80 ± 8.26 respectively. For the TGA analysis, the first region of degradation is due to the loss of water content in the sample while the second and the third region is the decomposition of the main chemical chain and the decomposition of the main ring. The bond that had been detected in the sample tested are the O-H stretching, the C-H bending of CH2 and the C-O-C bond. The viscosity obtained from the conducted test were 3337 cP, 3959 cP, 1284 cP and 82 cP for respectively. The conclusion that can be made is the 60:40 of the PVA:starch sample produced the best fiber based on the observation on the morphology, thermal properties and chemical properties. Faculty of Industrial Sciences and Technology Dissertations Universities and Colleges Dissertations Theses http://ecollib.ump.edu.my/28018/ Access in library only 0 0 0 1 10000 10000 2019-09-04 0 FIST .F37 2017 r Bc. 0000119955 2019-09-04 00:00:00 1 2019-09-04 PSM 0 0 0 1 10000 10000 2019-09-04 0 CD 10888 | FIST .F37 2017 r Bc. 0000119956 2019-09-04 00:00:00 1 2019-09-04 PSM VIRTUA40 7409 7415 VTLSSORT0080*0200*0400*0900*1000*2450*2600*3000*5000*5020*5040*5200*6100*6500*6501*8560*9992