| 245 | 1 | 0 |
_aInvestigation the delay of crack using stop drilled holes on mild steel / _cRidzuan Shah Bin Razi Varathau Rajoo |
| 246 | 3 |
_aInvestigation the delay of crack using stop drilled holes on mild steel _h[electronic resource] |
|
| 260 |
_aKuantan, Pahang : _bUMP, _c2009 |
||
| 300 |
_axv, 59 p. : _bill. (some col.) ; _c30 cm. + _e1 computer disc |
||
| 502 | _aProject paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2009 | ||
| 504 | _aBibliography : p. 49 | ||
| 520 | 3 | _aMany failures in engineering applications or machine components have been caused by a crack initiated from points at which stress was concentrated. As the stress concentration level is higher than a critical value, continuous crack-growth results in failure in the machine components. Crack initiation behavior has been evaluated to prevent an early failure of machine equipment. Delaying the crack initiation is important for the maintenance of machine elements as well as for the detection of crack initiation. Hence, the main objective of this study is to investigate the delay of crack using stop drilled holes. The investigation was based on the diameter of the stop drilled holes and the arrangement of the stop drilled holes. Both experiment and finite element analysis were done in order to validate the result. The experiment was carried out by using tensile test to obtain maximum applied load to the specimen while the finite element analysis was analyzed by using ALGOR V22 software to obtain the stress of the specimen. The experimental results and the finite element analysis results show that the crack initiation life of the specimen was longer when the diameter of the stop drilled holes increased. The further the location of the stop drilled holes with the slits location, the longer crack initiation life of the specimen. Thus, the influence of the stop drilled holes on the crack initiation life has been evaluated. | |
| 650 | 0 |
_aMetals _xFatigue |
|
| 650 | 0 | _aStrains and stresses | |