245 1 0 _aInvestigation of thin wall ductile iron parameter /
_cMohd Khairi Bin Mohd Noor
246 3 _aInvestigation of thin wall ductile iron parameter
_h[electronic resource]
260 _aKuantan, Pahang :
_bUMP,
_c2009
300 _axiv, 50 p. :
_bill. (some col.) ;
_c30 cm. +
_e1 computer disc
502 _aProject paper (Bachelor of Mechanical Engineering with Manufacturing Engineering) -- Universiti Malaysia Pahang - 2009
504 _aBibliography : p. 47-48
520 3 _aThis thesis deals with thin wall ductile iron parameter.There are two main objectives of this research,firstly, to investigate the processing parameter of thin wall ductile iron by using Sandwich method and to investigate the process design parameter for thin wall ductile iron.The cast iron has graphite in a matrix called pearlitic. The graphite shape is flake which is has lower strength. The study of graphite changes from flake form to nodular form by adding magnesium ferrosilicon as inoculation agent is under consideration. The ductile iron form is enhanced in strength and other mechanical properties. However, the thickness of thin wall is related to the composition of the magnesium adding. Green sand casting is one of the method for converting cast iron to ductile iron.The thesis describes the method of green sand casting by using Sandwich technique to get the thin wall ductile iron sample. From the sample,the hardness test and composition of element is checked to determine the effect and mechanical properties of different thickness of thin wall ductile iron.
650 0 _aIron, Nodular
650 0 _aMetals
_xDuctility
650 0 _aMetal castings