245	1	0	_aEffect of aging on machinability of 6061 aluminium alloy / _cEmir Izwandy Dzulkafli
246	3		_aEffect of aging on machinability of 6061 aluminium alloy _h[electronic resource]
260			_aKuantan, Pahang : _bUMP, _c2010
300			_axiii, 50 p. : _bill.(some col.) ; _c30 cm. + _e1 computer disc
502			_aProject paper (Bachelor of Mechanical Engineering) -- Universiti Malaysia Pahang - 2010
504			_aBibliography : p. 48-49
520	3		_aThe main purpose of this project is to study the effect of aging on machinability of 6061 aluminium alloy and also to investigate the effect of variation aging time on machinability of 6061 aluminium alloy which has been heat treated to specific temperature. The effect investigated for the as received, solution heat treated (SHT) and solution heat treated with aged (SHTA) conditions during this study. The effect of different aging times which are 1 hour, 3 hours and 5 hours at 160°C and 200°C results the effect on the milling performances. The process that has been gone through the experiment are sample preparation, solution heat treated, aging at various times and temperatures, milling process, surface analysis, surface roughness and the Vickers hardness test. From the experiment, the sample is harder after gone through all the process. As the conclusion of all the experiments that have been done, the aging has affected the 6061 aluminium alloy in terms of the hardness, microstructure behaviour and the surface roughness of the specimens.
650		0	_aAluminum alloys _xHeat treatment
650		0	_aAluminum alloys _xMechanical properties