| 100 | 0 | _aNur Hamizah Minhat | |
| 245 | 1 | 0 |
_aInvestigation of brass microstructure and mechanical properties using metal casting / _cNur Hamizah Minhat |
| 246 | 3 |
_aInvestigation of brass microstructure and mechanical properties using metal casting _h[computer file] |
|
| 260 |
_aKuantan, Pahang : _bUMP, _c2010 |
||
| 300 |
_axiii, 53 p. : _bill. ; _c30 cm. + _e1 computer disc |
||
| 502 | _aProject paper (Bachelor of Mechanical Engineering with Manufacturing Engineering) -- Universiti Malaysia Pahang - 2010 | ||
| 504 | _aBibliography: p. 50-51 | ||
| 520 | 3 | _aBrass is a alloying of cooper and zine, alpha (a) brass are quite soft and ductile, the ductility of the a brasses actually increased zinc content. The maximum strength of brass is 538 Mpa attained at 44wt% zinc. while most brasses are nit normally ranked as 'heat tratable', some brasses of very closely controlled composition are cast or hot worked in the duplex a/B state and the annealed at about 450 C to convert the microstructure to an single phase of better resistance to corrosion by dezincification in aggressive supply waters. | |