245	1	0	_aEffect of carbon black loading on the mechanical properties of rubber vulcanizates / _cMohd Faisal Ahmad Shafawi
260			_aKuantan, Pahang : _bUMP, _c2010
300			_axiv, 36 p. : _bill. (some col.) ; _c30 cm. + _e1 CD-ROM
502			_aProject paper (Bachelor of Chemical Engineering) -- Universiti Malaysia Pahang - 2010
504			_aIncludes bibliographical references
520	3		_aThe effects of filler loading on the tensile and elongation at break of SMR 10 using a sulphur vulcanization system was studied. Carbon black (N220) was used as the fillers and the loading range was from 10 to 40 phr. Two Roll Mill (Model LS-22005) and 25 Ton Hot Cold Molding Press (Model LS22025) used for mixing and molding press. Both equipments were supplied by Lotus Scientific. Tensile and elongation at break were determined using a Universal Testing Machine (Model 133004600771) operating at 20 mm/min. Results show that, elongation at break decreases, but tensile strength, increase with filler loading. This observation is attributed to the rubber–filler interphaseinteraction of carbon black and rubber.
650		0	_aCarbon-black
650		0	_aRubber _xMechanical properties
650		0	_aRubber _xAdditives
999			_aVIRTUA40 _c3173 _d3179
999			_aVTLSSORT0080*0200*0400*0900*1000*2450*2600*3000*5020*5040*5200*6500*6501*6502*9992