_aFabrication of nickel-cobalt intermetallic nanotapes by electrospinning / _cNoor Athirah Ismail |
| 260 |
_aKuantan, Pahang : _bUMP, _c2016 |
||
| 300 |
_axv, 38 p. : _bill. (some col.), charts ; _c30 cm. + _e1 CD-ROM |
||
| 500 | _aFaculty of Industrial Sciences and Technology | ||
| 502 | _aProject Paper (Bachelor of Applied Science (Honor) Material Technology) -- Universiti Malaysia Pahang – 2016 | ||
| 504 | _aBibliography : p. 36-38 | ||
| 520 | 3 | _aThis dissertation thesis is on the fabrication of Nickel-Cobalt nanotapes prepared by electrospinning technique. Electrospinning is a nanofabrication technique in which a polymeric solution is allowed to pass through an electric field of intensity ~105 V/m. In this work, the precursor polymeric solution was prepared by dissolving equimolar nickel acetate (18 mmol) and cobalt acetate in 50 wt.% polyvinylpyrrolidone (Mol. Wt. 40,000) in ethanol. The viscosity of the above solution was measured using a viscometer; the viscosity of the solution was ~653 cP. This solution was electrospun using a commercial electrospinning unit at 24 kV with a solution injection rate 0.5 ml/h. The as-spun fibers were annealed in an argon atmosphere at ~450 – 550oC for 1 h, based on thermogravimetric analysis. The annealed materials were examined by X-ray diffraction (XRD) technique and field emission scanning electron microscopy (FESEM). The XRD measurements showed that the annealed samples were only partially crystallized and has a belt-like morphology. | |
| 610 | 2 | 0 |
_aFaculty of Industrial Sciences and Technology _xDissertations |
| 650 | 0 |
_aUniversities and Colleges _xDissertations |
|
| 650 | 0 | _aTheses | |
| 856 | 4 | 0 |
_uhttp://ecollib.ump.edu.my/id/eprint/28000 _zAccess in library only |
| 999 |
_aVIRTUA40 _c7641 _d7647 |
||
| 999 | _aVTLSSORT0080*0200*0400*0900*1000*2450*2600*3000*5000*5020*5040*5200*6100*6500*6501*8560*9992 | ||