Investigation of brass microstructure and mechanical properties using metal casting / Nur Hamizah Minhat

By:

Nur Hamizah Minhat

Material type: Text

TextPublication details: Kuantan, Pahang : UMP, 2010Description: xiii, 53 p. : ill. ; 30 cm. + 1 computer discISBN:

THE0007734(Local)

Other title:

Investigation of brass microstructure and mechanical properties using metal casting [computer file]

Subject(s):

Brass -- Metallurgy

Dissertation note: Project paper (Bachelor of Mechanical Engineering with Manufacturing Engineering) -- Universiti Malaysia Pahang - 2010 Abstract: Brass is a alloying of cooper and zine, alpha (a) brass are quite soft and ductile, the ductility of the a brasses actually increased zinc content. The maximum strength of brass is 538 Mpa attained at 44wt% zinc. while most brasses are nit normally ranked as 'heat tratable', some brasses of very closely controlled composition are cast or hot worked in the duplex a/B state and the annealed at about 450 C to convert the microstructure to an single phase of better resistance to corrosion by dezincification in aggressive supply waters.

Tags from this library: No tags from this library for this title. Log in to add tags.

Average rating: 0.0 (0 votes)

Holdings ( 2 )
Title notes ( 3 )

Holdings
Item type	Current library	Call number	Copy number	Status	Date due	Barcode
Final Year Report	UMPLIB PEKAN	TS565 .H36 2010 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000054053
Final Year Report	UMPLIB PEKAN	CD 5042 \| TS565 .H36 2010 rs Bc. (Browse shelf(Opens below))	1	Not for loan		0000054054

Project paper (Bachelor of Mechanical Engineering with Manufacturing Engineering) -- Universiti Malaysia Pahang - 2010

Bibliography: p. 50-51

Brass is a alloying of cooper and zine, alpha (a) brass are quite soft and ductile, the ductility of the a brasses actually increased zinc content. The maximum strength of brass is 538 Mpa attained at 44wt% zinc. while most brasses are nit normally ranked as 'heat tratable', some brasses of very closely controlled composition are cast or hot worked in the duplex a/B state and the annealed at about 450 C to convert the microstructure to an single phase of better resistance to corrosion by dezincification in aggressive supply waters.